Visoko temperaturno istraživanje svojstava koksa za visoke peći

The behavior of coke in the blast furnace is discussed in this article. The methods of taking charge coke samples from blast furnace have been verified. The tests of the effect of temperature on coke (subjected to laboratory tests reproducing, to a certain extent, the conditions prevailing at the tuyere level of the blast furnace) have established factors responsible for the degradation of coke. This has allowed the parameters characterizing the structure to be described as follows: Lc, the crystallite height is contained in range 1.5932 - 3.2620 nm; La, the crystallite width is in the range 2.82013 - 5.7737 nm; and the crystallinity factor, Wk, is contained in the range 0.147 - 0.77014.U radu se raspravlja o ponašanju visoko-pećnog koksa. Za uzimanje koksa iz visoke peći koristile su se razne metode. Ispitivanje učinaka temperature na koks (izloženog laboratorijskoj ispitnoj proizvodnji, do određene mjere, uvjeti koji pretežu na razini duvnice) daju faktore odgovorne za raspad koksa. To je omogućilo nastajanje takvih parametara zahvaljujući kojima se formira struktura prema slijedećem opisu: Lc, visina kristala u rasponu od 1.5932 - 3.2620 nm; La, širina kristala je u rasponu od 2.82013 - 5.7737 nm; a faktor kristaličnosti Wk u opsegu od 0.147 - 0.77014