Utjecaj sastava zaštitnog plina pri MIG postupku zavarivanja na mehanička svojstva niskougljičnih čelika

The present study is focused on the mechanical properties of the deposited material which was extracted from welded region. This study explains the effect of the shielding gas composition on tensile behavior, R = - 1 fatigue response and various tempe-rature impact test results of MIG welded low carbon steels. In tensile tests, the stre-ngth values are increased with increase of CO2 content, whereas the ductility is decreased. In the fatigue tests, the fatigue strength and the number of cycles to failure enhanced as the content of CO2 increased. However, the impact toughness of the filler material is seriously influenced by the content of the shielding gas. An increase in CO2 content caused significant decrease in toughness values at all temperatures.Ovaj rad se usredotočio na mehanička svojstva dodatnog materijala uzetog iz zavarenog područja. Rad objašnjava utjecaj sastava zaštitnog plina na vlačnost, R = -1 zamor i rezultate ispitivanja žilavosti na raznim temperaturama niskougljičnih čelika zavarenih metodom MIG. U testovima za ispitivanje vlačne čvrstoće vrijednosti čvrstoće su povećane kao rezultat povećanog sadržaja CO2, a plastičnost je smanjena. U testovima za ispitivanje zamora povećala se dinamička čvrstoća kao i broj ciklusa prije pucanja zajedno s povećanom količinom CO2. Međutim, žilavost materijala za dodavanje jako ovisi o zaštitnom plinu. Povećanje količine CO2 značajno smanjuje žilavost na svim temperaturama