Mechanical Behavior of Alumina Reinforced with Carbon-Coated Silicon Carbide Whiskers

SiC whiskers with 0, 20, and 50 Å carbon coatings were incorporated into an alumina matrix to modify residual thermal stress and interfacial bonding. Composites were characterized using triaxial X-ray diffraction for residual stress determination and electron microscopy to explore interfacial chemistry. Fracture toughness and R-curve behavior were examined for short and long crack lengths. Uncoated SiC whiskers optimized strength, fracture toughness, and R-curve behavior of these composites. A graphite interphase at the whisker/matrix interface decreased contributions to crack bridging without promoting additional toughening by whisker pullout