VALORACIÓN DE ACETINAS COMO REEMPLAZO PARCIAL DE ACEITE NAFTÉNICO EN COMPUESTOS DE CAUCHO SBR1502

In this investigation, technical grade glycerin as a byproduct of the biodiesel industry was esterified to obtain mono, di, tri acetyl glycerols. Glacial acetic acid and ion exchange resin Amberlyst®15 was used as a heterogeneous catalyst to perform the reaction. Acetyl glycerols were tested to partially replace up to 10 parts by weight naphthenic oil in SBR 1502 composites reinforced with precipitated silica. Dicumyl peroxide was used as a crosslinker agent. The rheometer testing was done at rubber blends before prior to curing. Tensile strength, elongation at break and tear strength were evaluated for cured composites. It was determined that the addition of 10 phr of acetyl glycerols slightly affected the minimum torque and tensile strength.En esta investigación, glicerina grado técnico proveniente de la industria del biodiesel se esterificó para obtener mono, di, tri acetil gliceroles. Se empleo ácido acético glacial y resina de intercambio iónico Amberlyst®15 como catalizador heterogéneo para llevar a cabo la reacción. Acetil gliceroles fueron probados para reemplazar parcialmente hasta 10 partes en peso de aceite nafténico en formulaciones de caucho SBR1502 reforzado con sílica precipitada. Se uso peróxido de dicumilo para curar los compuestos. Se realizaron ensayos de reometría a los compuestos antes de ser curados. La resistencia a la tracción, elongación a rotura y resistencia al desgarre fueron evaluados para los compuestos curados. Se determinó que la adición de 10 phr de acetil gliceroles afectó levemente el torque mínimo y la resistencia a la tracción