Influence of transition metal charge compensation species on phase assemblage in zirconolite ceramics for Pu immobilisation

Immobilisation of Pu in a zirconolite matrix (CaZrTi2O7) is a viable pathway to disposition. A-site substitution, in which Pu4+ is accommodated into the Ca2+ site in zirconolite, coupled with sufficient trivalent M3+/Ti4+ substitution (where M3+ = Fe, Al, Cr), has been systematically evaluated using Ce4+ as a structural analogue for Pu4+. A broadly similar phase assemblage of zirconolite-2M and minor perovskite was observed when targeting low levels of Ce incorporation. As the targeted Ce fraction was elevated, secondary phase formation was influenced by choice of M3+ species. Co-incorporation of Ce/Fe resulted in the stabilisation of a minor Ce-containing perovskite phase at high wasteloading, whereas considerable phase segregation was observed for Cr3+ incorporation. The most favourable substitution approach appeared to be achieved with the use of Al3+, as no perovskite or free CeO2 was observed. However, high temperature treatments of Al containing specimens resulted in the formation of a secondary Ce-containing hibonite phase