Parasitic phases at the origin of magnetic moment in BiFeO3 thin films grown by low deposition rate RF sputtering

FUNDAÇÃO DE AMPARO À PESQUISA DO ESTADO DE SÃO PAULO - FAPESPCONSELHO NACIONAL DE DESENVOLVIMENTO CIENTÍFICO E TECNOLÓGICO - CNPQA series of epitaxial BiFeO3 thin films has been grown under high partial pressure in a pure O-2 atmosphere, which leads to a low deposition rate. The samples grown under these conditions have presented an evolution of the quality of the epitaxy as the deposition temperature increases, however, spurious beta-Bi2O3 and supertetragonal BiFeO3 phases are present in the films grown at higher temperatures. The presence of gamma-Fe2O3 is reported in one growing condition, and has been attributed to the origin of hysteretic ferromagnetic behavior. A second kind of magnetism, with higher magnetic moment and anhysteretic behaviour, is attributed to the presence of mixed phases of BiFeO3.1221215FUNDAÇÃO DE AMPARO À PESQUISA DO ESTADO DE SÃO PAULO - FAPESPCONSELHO NACIONAL DE DESENVOLVIMENTO CIENTÍFICO E TECNOLÓGICO - CNPQFUNDAÇÃO DE AMPARO À PESQUISA DO ESTADO DE SÃO PAULO - FAPESPCONSELHO NACIONAL DE DESENVOLVIMENTO CIENTÍFICO E TECNOLÓGICO - CNPQ2012/18397-12012/51198-2309354/2015-3This work was supported by FAPESP (Project No. 2012/51198-2). Some of the XRD measurements were performed at the XRD2 beamline of the LNLS/CNPEM under Project Nos. 20150162 and 20160908. The authors thank the LNNano/CNPEM for XRD/XRR, AFM and sputtering facilities, the LIEC/UFSCar for the SQUID measurements, and M. M. Soares for important discussions regarding the structural characterization. P.S. thanks FAPESP for financial support (Project No. 2012/18397-1). J.C.C. acknowledges support from CNPq (Project No. 309354/2015-3)