Interlayer conformations of intercalated dodecyltrimethylammonium in rectorite as determined by ftir, xrd, and tg analyses

Intercalation of a wide variety of alkylammonium cations into the interlayer spaces of swelling clay minerals leads to many different applications, ranging from surface-charge measurements to rendering the clay compatible for the preparation of clay nanocomposites, but knowledge of the exact conformation of the intercalated organic species is still incomplete, thus preventing a full understanding of this process. The purpose of this study was to investigate the interlayer conformation of dodecyltrimethylammonium (DDTMA) bromide in rectorite as affected by the amounts of DDTMA intercalated, using a battery of physical and spectroscopic methods. The capacity of rectorite to intercalate DDTMA was equivalent to 1.67 times the cation exchange capacity (1.67 CEC) of the mineral even though the initial input was as much as 5.00 CEC. When the DDTMA intercalated was d. They became integral at 1.67 CEC. The results suggest that the mineral might be composed of mixed layers of a monolayer intercalated rectorite and a trilayer intercalated rectorite, without a bilayer as intermediate, when the amount of DDTMA intercalated was between 0.5 and 1.67 CEC