Improving effect of poly (linolenic acid)-g-poly (caprolactone)-g-poly (t-butyl acrylate) interfacial layer on Au/n-Si diodes

Gokcen, Muharrem/0000-0001-9063-3028WOS: 000433648600001Poly (linolenic acid)-g-poly (caprolactone)-g-poly (t-butyl acrylate) (PLiIPCLPtBA) graft copolymer was used as an interfacial layer in Au/n-Si Schottky diode. The novel PLiIPCLPtBA layer was coated on n-Si single crystal wafer through an electrospinning system. Nanofiber characteristics of the PLiIPCLPtBA layer was obtained by a Field Emission Scanning Electron Microscope (FEG-SEM). The current-voltage (I-V) measurements of these AO-Si diodes with and without polymeric layer were conducted in dark and under various illumination intensity levels (halogen lamp) at room temperature. Main electrical parameters such as series resistance (R-s), shunt resistance (R-sh), ideality factor (n), reverse saturation current (I-o), zero-bias barrier height (Phi(bo)) and interface state density (N-ss) of the structures were extracted from forward-bias I-V data. (C) 2018 Elsevier B.V. All rights reserved.Duzce University Scientific Research ProjectDuzce University [2014.05.02.260, 2015.05.03.381]This work is supported by Duzce University Scientific Research Project (project numbers 2014.05.02.260, 2015.05.03.381)