Development of process parameters for selective laser melting of a Zr-based bulk metallic glass

Parameters for selective laser melting of Zr59.3Cu28.8Al10.4Nb1.5 (trade name AMZ4), allowing crack-free bulk metallic glass with low porosity, have been developed. The phase formation was found to be strongly influenced by the heating power of the laser. X-ray amorphous samples were obtained with laser power at and below 75 W. The as-processed bulk metallic glass was found to devitrify by a two-stage crystallization process within which the presence of oxygen was concluded to play an essential role. At laser powers above 75 W, the observed crystallites were found to be a cubic phase (Cu2Zr4O). The hardness and Young’s modulus in the as-processed samples was found to increase marginally with increased fraction of the crystalline phase