Magnetocaloric and Magnetic Properties of Meta‐Magnetic Heusler Alloy Ni41Co9Mn31.5Ga18.5

Ni41Co9Mn31.5Ga18.5 is a magnetic Heusler alloy, which indicates metamagnetic transition at the reverse martensite transition. In this paper, caloric measurements were performed and discussed about magnetocaloric effect. We also performed magnetization measurements around Curie temperature TC in the martensite phase and analyzed by means of the spin fluctuation theory of itinerant electron magnetism. From the differential scanning calorimetry (DSC) measurements in zero fields, the value of the latent heat λ was obtained as 2.63 kJ/kg, and in magnetic fields the value was not changed. The entropy change ΔS was − 7.0 J/(kgK) in zero fields and gradually increases with increasing magnetic fields. The relative cooling power (RCP) was 104 J/kg at 2.0 T, which was comparable with In doped Ni41Co9Mn32Ga16In2 alloy