Transmission electron microscopy structure and platinum-like temperature coefficient of resistance in a ruthenate-based thick film resistor with copper oxide

As an alternative to thin-film platinum temperature sensor elements, thick film resistor ones are of interest for circuits which can withstand a near-engine environment. From a pyrochlore paste (DuPont 5091D), a close match is obtained (after firing) to the positive temperature coefficient of resistance (TCR) of Pt. Within the glassy matrix during 850 °C850 °C firing, needle-like RuO2RuO2 grains grow by a mechanism consistent with periodic bond chain theory. The acicular growth habit is attributed to a Cu2OCu2O additive, which is assumed to oxidize upon firing. The needles provide direct paths for metallic conduction and a characteristic positive TCR to the thick film in spite of having a low RuO2RuO2 volume fraction. © 2000 American Institute of Physics.Peer Reviewedhttp://deepblue.lib.umich.edu/bitstream/2027.42/70506/2/JAPIAU-88-2-1124-1.pd