Characteristic thermal transitions of zinc oxide and eugenol materials were compared with those of zinc eugenolate.Peer Reviewedhttp://deepblue.lib.umich.edu/bitstream/2027.42/66654/2/10.1177_00220345710500025301.pd
Peer Reviewedhttp://deepblue.lib.umich.edu/bitstream/2027.42/67370/2/10.1177_00220345610400012201.pd
An experimental reinforced zinc oxide-eugenol cement of compressive strength 8,000 to 9,200 psi (562...
Uptake of eugenol from eugenol-containing temporary materials may reduce the adhesion of subsequent ...
Characteristic thermal transitions of zinc oxide and eugenol materials were compared with those of z...
Previous studies in this laboratory showed that addition of o-ethoxybenzoic acid (EBA) improved the ...
Zinc oxide-eugenol cement is well tolerated by the tissues. ' It acts as a palliative on the de...
The purpose was to evaluate polymerization as an approach to strengthening zinc oxide-eugenol (ZOE) ...
The purpose was to evaluate polymerization as an approach to strengthening zinc oxide-eugenol (ZOE) ...
Master of ScienceProsthodonticshttps://deepblue.lib.umich.edu/bitstream/2027.42/147972/1/ot_148.pd
The structure of eugenol, zinc eugenolate salt, zinc oxide-eugenol and guaiacol ce-ments, and deuter...
The palliative effect of zinc oxide and eugenol on the pulp, when used as a base or temporary fillin...
Peer Reviewedhttp://deepblue.lib.umich.edu/bitstream/2027.42/67707/2/10.1177_00220345660450022801.pd
The continuous leaching of eugenol from zinc oxide-eugenol cements causes the weak zinc eugenolate c...
Master of Science (MS)Prosthodonticshttps://deepblue.lib.umich.edu/bitstream/2027.42/147972/1/ot_148...
The microstructure of zinc oxide-eugenol cement and the water-leached product was examined by electr...
Peer Reviewedhttp://deepblue.lib.umich.edu/bitstream/2027.42/67370/2/10.1177_00220345610400012201.pd
An experimental reinforced zinc oxide-eugenol cement of compressive strength 8,000 to 9,200 psi (562...
Uptake of eugenol from eugenol-containing temporary materials may reduce the adhesion of subsequent ...
Characteristic thermal transitions of zinc oxide and eugenol materials were compared with those of z...
Previous studies in this laboratory showed that addition of o-ethoxybenzoic acid (EBA) improved the ...
Zinc oxide-eugenol cement is well tolerated by the tissues. ' It acts as a palliative on the de...
The purpose was to evaluate polymerization as an approach to strengthening zinc oxide-eugenol (ZOE) ...
The purpose was to evaluate polymerization as an approach to strengthening zinc oxide-eugenol (ZOE) ...
Master of ScienceProsthodonticshttps://deepblue.lib.umich.edu/bitstream/2027.42/147972/1/ot_148.pd
The structure of eugenol, zinc eugenolate salt, zinc oxide-eugenol and guaiacol ce-ments, and deuter...
The palliative effect of zinc oxide and eugenol on the pulp, when used as a base or temporary fillin...
Peer Reviewedhttp://deepblue.lib.umich.edu/bitstream/2027.42/67707/2/10.1177_00220345660450022801.pd
The continuous leaching of eugenol from zinc oxide-eugenol cements causes the weak zinc eugenolate c...
Master of Science (MS)Prosthodonticshttps://deepblue.lib.umich.edu/bitstream/2027.42/147972/1/ot_148...
The microstructure of zinc oxide-eugenol cement and the water-leached product was examined by electr...
Peer Reviewedhttp://deepblue.lib.umich.edu/bitstream/2027.42/67370/2/10.1177_00220345610400012201.pd
An experimental reinforced zinc oxide-eugenol cement of compressive strength 8,000 to 9,200 psi (562...
Uptake of eugenol from eugenol-containing temporary materials may reduce the adhesion of subsequent ...