Predicting the linear viscoelastic properties of monodisperse and polydisperse polystyrenes and polyethylenes

For linear homopolymers the linear viscoelastic predictions of the double reptation model are compared to those of a recent, more detailed model, the “dual constraint model” and to experimental data for monodisperse, bidisperse, and polydisperse polystyrene melts from several laboratories. A mapping procedure is developed that links the empirical parameter K of the double reptation model to the molecular parameter τ e of the dual constraint model, thereby allowing the parameter K to be related to molecular characteristics such as the monomeric friction coefficient ζ. Once K (or τ e ) are determined from data for monodisperse polymers, the double reptation model predicts that for fixed weight-average molecular weight M w , the zero-shear viscosity η 0 increases slightly with increasing polydispersity M w /M n for log normal distributions, while for the dual constraint model η 0 is almost independent of M w /M n . Experimental data for polystyrenes show no increase (or even a slight decrease) in η 0 with increasing M w /M n at fixed M w , indicating a deficiency in the double reptation model. The dual constraint theory is also applied to hydrogenated polybutadienes and commercial high-density polyethylenes, where we believe it can be used to indicate the presence of long side branches, which are difficult to detect by other analytic methods.Peer Reviewedhttp://deepblue.lib.umich.edu/bitstream/2027.42/42206/1/397-40-6-516_10400516.pd