Correlations between microstructure and room temperature tensile behavior of a duplex TNB alloy for systematically heat treated samples

The mechanical properties of TiAl alloys are very sensitive to the inherent microstructure. For an in-depth understanding of microstructural influences on mechanical properties a duplex type TNB (Nb-containing TiAl) alloy has been investigated. For varying the microstructure of this alloy controlled heat treatments (HT) have been performed with eight distinct maximum temperatures, ranging from 1230 degrees C to 1300 degrees C with a 10 degrees C temperature increment. The series of annealing processes resulted in duplex microstructures with a gradual change of the ratio of globular grains and lamellar colonies, keeping the global chemical composition unchanged. Microstructure of each sample was characterized using SEM and TEM before and after mechanical testing to correlate the morphology and microstructure features to the tensile properties. Quantitative data analysis from these results revealed how the evolution of duplex microstructures influences the room temperature tensile properties: i.e. the elastic stiffness, room temperature ductility, work hardening, fracture stress, and fracture strain. The results are discussed with respect to deformation mechanisms as understood from the tensile test results and fracture surface investigations. From the observed correlations between microstructure and properties an optimized constellation of globular and lamellar microstructure for relevant properties can be predicted. Furthermore, the required heat-treatment window for properties targeted can be defined