Cavitation damage prediction

New results from cavitating venturi water tests were used to reinforce the concept of cavitation erosion efficiency previously developed from tests in a vibratory facility with both water and sodium. The concept emerges from a technique which allows a priori prediction of eventual cavitation erosion rates in flow machines. Bubble collapse pulse height spectra obtained from submerged microprobes are correlated with measured erosion rates in given laboratory and/or field devices to allow this prediction. Preliminary results from such correlations are presented together with other measurements of the effects of gas content, velocity and cavitation condition upon the mechanical cavitation intensity as measured by the pulse height spectra.New results from vibratory facility tests in tap water and synthetic seawater upon three materials of variable corrodability (304 stainless steel, 1018 carbon steel and 1100-0 aluminum) are presented. The ratio between maximum erosion rates for the saltwater and freshwater tests were found to increase toward unity as the mechanical cavitation intensity is increased, i.e. increased mean depth to penetration (MDPR), as expected on theoretical grounds.The relation between the incubation period and MDPRmax was examined from the vibratory test results, and was found to depend upon the material properties as well as the fluid flow conditions.Peer Reviewedhttp://deepblue.lib.umich.edu/bitstream/2027.42/23641/1/0000605.pd