Charakterizace molekulární struktury emulzních akrylátových mikrogelů: studium vlivu molekulové hmotnosti na vlastnosti nátěrů tvořených samosíťujícími latexy

Self-crosslinkable latexes of coreshell microgel particles were synthesized by the emulsion polymerization of acrylic monomers. The molar mass of copolymers forming the shell layer was gradually reduced by isooctyl 3-mercaptopropionate included in the synthesis of the shell layers. The molar mass distribution of latex particles was determined using size exclusion chromatography and asymmetric flow field flow fractionation, respectively, both separation methods being coupled with a multi-angle light scattering detector. The results confirmed theoretical predictions and described empirically the effects of molar mass of the shell layer copolymer on decreasing the minimum film-forming temperature and influencing the end-use properties of coatings.Samosíťující latexy na bázi coreshell mikrogelových částic byly syntetizovány emulzní polymerací akrylátových monomerů. Molekulová hmotnost kopolymerů tvořících obal byla postupně snižována pomocí izooktyl-3-merkaptopropionátu. Distribuce molekulové hmotnosti byla stanovena pomocí gelové permeační chromatografie a frakcionace tokem v asymetrickém tokovém poli, obě metody spojené s detektorem víceúhlového rozptylu světla. Výsledky potvrdily teoretické předpoklady a ukázaly, že i malý přídavek regulátoru molekulové hmotnosti vedl k podstatnému snížení minimální filmotvorné teploty a poklesu citlivosti vůči vodě vzniklých nátěrových filmů