Add to ORKGThis contribution contains the results of measurement of carbon redistribution ithe welded joint of low-alloy CrNiMoV steel and low-alloy Si steel. The measurements was carried out in the range of temperatures 500-1000°C. On the basis of the measured concentration data the carbon diffusion coefficients were calculated and also their temperature dependences were determine
The steel carburizing process over the temperature range of 850-1100°C is studied. The different ana...
AbstractThe paper deals with assessment of influence of welding time on welding joint creation. Diff...
An original results of redistribution in welded joints of unalloyed 12050+Al steel and high alloy au...
This contribution contains the original results of measurement of redistribution of carbon in the we...
Measurement of carbon redistribution was carried out in temperature range 500-750oC in two types of ...
The redistribution of carbon in steel weldments heated at temperatures situated in the range 500 °C ...
The diffusion specimens were isothermally annealed in the temperature range of 500 to 1100řC interva...
Content of a document result measurements and analysis carbon´s diffusion at welding joint created f...
Measurements of Al, Cr, Fe, Ni and C diffusion in steel welded joints of the modified 12050 steels a...
Carbon diffusion was studied in temperature interval 573 - 1073 K in carbon-supersaturated surface l...
Especially in heat treatment and hot forming of high-strength low-alloyed steels or cast iron, e.g. ...
This contribution deals with the mutual relation of the thermodynamic and diffusion interaction coef...
The paper deals with original methodology for characterization of chemical heterogeneity of welded j...
In this paper, the results of diffusion C and Mn measurements in diffusion couples in steels with c...
In this paper results of measurements of simultaneous diffusion of aluminium, carbon, chromium, iron...
The steel carburizing process over the temperature range of 850-1100°C is studied. The different ana...
AbstractThe paper deals with assessment of influence of welding time on welding joint creation. Diff...
An original results of redistribution in welded joints of unalloyed 12050+Al steel and high alloy au...
This contribution contains the original results of measurement of redistribution of carbon in the we...
Measurement of carbon redistribution was carried out in temperature range 500-750oC in two types of ...
The redistribution of carbon in steel weldments heated at temperatures situated in the range 500 °C ...
The diffusion specimens were isothermally annealed in the temperature range of 500 to 1100řC interva...
Content of a document result measurements and analysis carbon´s diffusion at welding joint created f...
Measurements of Al, Cr, Fe, Ni and C diffusion in steel welded joints of the modified 12050 steels a...
Carbon diffusion was studied in temperature interval 573 - 1073 K in carbon-supersaturated surface l...
Especially in heat treatment and hot forming of high-strength low-alloyed steels or cast iron, e.g. ...
This contribution deals with the mutual relation of the thermodynamic and diffusion interaction coef...
The paper deals with original methodology for characterization of chemical heterogeneity of welded j...
In this paper, the results of diffusion C and Mn measurements in diffusion couples in steels with c...
In this paper results of measurements of simultaneous diffusion of aluminium, carbon, chromium, iron...
The steel carburizing process over the temperature range of 850-1100°C is studied. The different ana...
AbstractThe paper deals with assessment of influence of welding time on welding joint creation. Diff...
An original results of redistribution in welded joints of unalloyed 12050+Al steel and high alloy au...