Characteristics of novel dental composites containing 2,2-bis[4-(2-methoxy-3-methacryloyloxy propoxy) phenyl] propane as a base resin.

Many dental restorative dental composites still utilize 2,2-bis[4-(2-hydroxy-3-methacryloyloxy propoxy) phenyl] propane (Bis-GMA) as base resin. The high viscosity of Bis-GMA necessitates dilution with dimethacrylate ethers of low viscosity such as triethylene glycol dimethacrylate (TEGDMA). However, increased amounts of the TEGDMA have adverse effects on properties such as water uptake and curing shrinkage. The viscosity of the base resin should be as low as possible to enable the preparation of dental composites with a minimum content of diluent. To overcome the disadvantage of Bis-GMA, i.e., its high viscosity caused by hydrogen bonding between hydroxyl groups, 2,2-bis[4-(2-methoxy-3-methacryloyloxy propoxy) phenyl propane (Bis-M-GMA) was prepared by substituting methoxy groups for hydroxyl groups in Bis-GMA. The viscosity of Bis-GMA was dramatically decreased from 574 (Pa.s) to 3.7 (Pa.s) by substitution of methoxy group. Consequently, the amount of TEGDMA included in the resin matrix could be minimized. Dental composites were prepared from Bis-M-GMA (or Bis- GMA) mixtures with TEGDMA filled with 75 wt % filler. Comparing the curing shrinkage of dental composite containing Bis-M-GMA with that prepared from Bis-GMA, the reduction in curing shrinkage was about 47%. Dental composites prepared from new resin matrixes also exhibited low water uptake and better properties in mechanical strength.This study was supported by a grant of the Korea Health 21 R&D Project, Ministry of Health & Welfare, Republic of Korea. (03-PJ1-Ch09-0001