Effect of M²⁺-cation (M²⁺=Zn and Cd) on perovskite synthesis and structural parameters of Ba (M_1/3Nb_1/3Ta_1/3)O₃ceramics

869-872Polycrystalline samples of Ba(Zn1/3Nb1/3Ta1/3)O3 and Ba(Cd1/3Nb1/3Ta1/3)O3 have been prepared by solid state reaction technique. Preliminary X-ray studies showed the formation of single-phase compound. Zinc doped barium niobium tantalet had a cubic unit cell and cadmium doped barium niobium tantalet had a tetragonal structure. The d-values and intensities for each reflection were computed using the lattice parameters, which agree well with the observed values. The calculated and order line intensities for both compounds decreased in the ordered which is expected from the differences in the atomic scattering factor of B-ions, thus confirms the 1:1 degree of cation ordering