Thermal degradation and stability of wood particle composites deployed as decorative components

The contribution aims to design, deliver and debate on thermal degradation and thermal stability of several wood/PP composite materials. The wood polymer-based composites (n. WPCs) were manufactured through injection moulding by deploying various wood species under 10% and 40% weight fraction within the thermoplastic matrix. Thermal degradation of WPC specimens revealed similarities in characteristics, small discrepancies in the degradation temperatures but higher contents in the char formation, between 10% to 35% with wood content increase