Transport properties of the metallic state of TMTSF-DMTCNQ

We report the transport properties (longitudinal and transverse conductivity, magnetoresistance and thermopower) of TMTSF-DMTCNQ for pressures up to 13 kbar and temperatures down to 1.2 K together with the phase diagram which results from these measurements. The most striking results are the occurrence of a first order insulator-metal low temperature transition as pressure is increased above 9.75 kbar and the properties of the metallic state. At pressures sufficiently high to quench the Peierls transition the helium temperature conductivity is greater than that found in any organic conductor at any temperature (σ∥ ≳ 105 (Ωcm)-1) and an enormous magnetoresistance (Δρ/ρ0 ~ 15) is found for a field of 75 kOe perpendicular to the conducting chains.Nous présentons des mesures des propriétés de transport (conductibilité longitudinale et transversale, magnétorésistance et pouvoir thermoélectrique) dans le composé TMTSF-DMTCNQ sous pression jusqu'à 13 kbar et à basse température jusqu'à 1,2 K. Un diagramme de phases a été obtenu à partir de ces mesures. Les résultats les plus frappants sont : l'existence d'une transition isolant-métal du premier ordre à 9,75 kbar pour une pression croissante et les propriétés de l'état métallique. A des pressions suffisamment élevées pour faire disparaitre la transition de Peierls la conductibilité atteint à la température de l'hélium liquide une valeur supérieure à ce qui a été observé jusqu'à présent dans un conducteur organique à n'importe quelle température (σ|| ≳ 105 (Ωcm) -1). De plus, une magnétorésistance très importante (Δρ/ρ 0 ~ 15) est détectée lorsqu'un champ de 75 kOe est placé perpendiculairement aux chaînes conductrices