Defect morphology in a biaxial thermotropic polymer

Optical observations of the thread texture of a nematic thermotropic polymer commercially known as VECTRA B950$^{\circledR}$ have shown the existence of three types of half integer disclination lines, called here $E_{x}, E_{y}$ and $E_{z}$, sometimes associated with integer disclination lines. This plurality of defects is typical of the biaxial nature of this nematic phase, due to interchain rotational correlations between phenyl rings. The relationships between defects which arise from the topological theory are confirmed, in static as well as in dynamic experiments. During shear flow, there is a splitting of $E_{y}$ into $E_{x}$ and $E_{z}$ at a shear deformation lower than that corresponding to the multiplication of $E_{x}$ and $E_{z}$ defects.Les observations optiques de la texture à fils d'un polymère thermotrope nématique, commercialisé sous la référence VECTRA B950$^{\circledR}$, ont montré l'existence de trois types de lignes de disinclinaisons, appelées ici $E_{x}, E_{y}$ et $E_{z}$, de rang demi-entier, parfois associées à des lignes entières. La pluralité de ces défauts est caractéristique de la nature de cette phase nématique biaxe, reliée à des corrélations de rotation interchaînes entre les plans aromatiques. Les relations topologiques entre défauts caractéristiques de la phase biaxe sont vérifiées dans les situations statiques aussi bien que dynamiques. Durant un écoulement de cisaillement, il ya une séparation de $E_{y}$ en $E_{x}$ et $E_{z}$, à une déformation plus petite que celle correspondant à la multiplication des défauts $E_{x}$ et $E_{z}$