Influence of Strain Rate and Temperature on the Structure. Property Behavior of High-Purity Titanium

The effect of strain rate, temperature, grain size, and texture on the substructure and mechanical response of high-purity polycrystalline titanium is presented. The compressive stress-strain response of 20 and 240 µm grain size high-purity Ti was found to depend on both the applied strain rate ; 0.001 ≤ dε/dt ≤ 7500 s-1, and the test temperature ; 77 ≤ T ≤ 873 K. The rate of strain hardening in Ti is seen to increase with increasing strain rate. The substructure of high-purity Ti deformed at high-strain-rate or quasi-statically at 77K displayed a higher incidence of deformation twinning than during quasi-static deformation at 298K.Nous présentons l'influence de la vitesse de déformation, dε/dt, de la température, T, et de la taille de grain, d, et de la texture sur l'évolution de la microstructure et sur la réponse mécanique d'un titane polycristallin de haute pureté. Pour d variant entre 20 et 240 µm, nous trouvons que la réponse en compression du titane dépend à la fois de dε/dt, pour 0.001 ≤ dε/dt ≤ 7500 s-1, et de T , pour 77 ≤ T ≤ 873 K. Nous avons établi que le taux d'écrouissage augmente avec la vitesse de déformation. La microstructure du titane montre que la déformation par mâclage est plus importante à 77 K, sous sollicitation dynamique ou quasi statique, qu'après déformation quasi statique à 298K