The conductivity of alloyed radical anion salts : 2,5-disubstituted DCNQI's with copper-counterions

We have performed conductivity measurements on a series of binary and ternary copper-salts from differently substituted R, R' — N, N'-dicyano-quinonediimines (DCNQI's ). At room temperature they all have a high conductivity, which is preserved partly down to the lowest temperatures. In comparison with the (unalloyed) single complex crystals in these alloys disorder effects shift phase transition temperatures and reduce the magnitudes of the conductivity. In two cases dips of the T-dependent conductivity appear below 50 K. They are explained by a metal-semiconductor transition accompanied by a reentrance into the metallic state at even lower temperatures, in analogy to similar results on (2,5-Me, Me-DCNQI)2Cu under applied pressure.Nous présentons des mesures de conductivité effectuées sur une série de sels binaires et ternaires de cuivre avec les différentes substitutions des molécules R, R' — N, N'-dicyanoquinonediimines (DCNQI's). La conductivité de tous ces sels est élevée à haute temp£rature et le demeure en partie jusqu'aux températures les plus basses. La comparaison avec le comportement des cristaux du complexe simple indique que le désordre déplace les températures de transition et réduit la conductivité. Pour deux cas, des minima de la conductivité sont observés au-dessous de 50 K. Ce comportement est interprété par l' existence d'une transition métal-semiconducteur suivie d'une réapparition de l'état conducteur à plus basses températures d'une manière similaire à ce qui a été observé avec le composé (2,5-Me, Me-DCNQI)2Cu sous pression