Variations des propriétés optiques de couches minces d'or en fonction de leur vitesse de formation

A study has been made of the influence of the speed of formation on the optical properties of evaporated gold films. Three series of evaporated layers have been prepared respectively with a speed of 08, 3 and 25 mμ by minute. Evaporated films of similar series, the thickness of which varied from 0 to 70 mμ, have been prepared during two evaporations made as nearly as possible at the same speed. It was found that the optical properties vary a great deal according to the speed of formation. Specially, the absorption A' of a 60 mμ thick film may be multiplied by 25 when the speed of formation is increased from 25 to 0.8 mμ by minute.On a étudié l'influence, sur les propriétés optiques de couches minces d'or obtenues par évaporation, de la vitesse de formation du dépôt. On a utilisé pour cela trois séries de couches préparées respectivement avec des vitesses de formation de 0,8, 3 et 25 mμ à la minute. Toutes les couches d'une même série, dont les épaisseurs variaient entre 0 et 70 mμ, ont été préparées au cours de deux évaporations conduites pratiquement à la même vitesse. On montre que les propriétés optiques des couches varient beaucoup avec la vitesse de projection. En particulier l'absorption A' d'une couche d'or de 60 mμ. d'épaisseur peut être multipliée par 25 lorsque la vitesse de formation passe de 25 à 0,8 mμ à la minute