Thermal anomaly in sodium potassium sulphate crystals

The thermal properties of NaKSO4 crystal, grown at 315 K by the slow evaporation method, were studied in the 300-500 K temperature range by performing Thermomechanical (TMA), Thermogravimetry (TG), Differential Thermal Analysis (DTA) and Differential Scanning Calorimetry (DSC) measurements. Thermal expansion coefficients for the three fundamental crystallographic directions showed anomalous behaviour around 453 K. Also, in this temperature range, anisotropic effects were observed and a weight loss was not detected. The DSC measurements of the specific heat at constant pressure Cp, showed a slight continuous increase with increasing temperature and a peak at 453 K.Les propriétés thermales du NaKSO4 cristal, que l'on a fait croître à 315 K par la méthode d'évaporation lente, ont été étudiées dans l'intervalle de température entre 300 et 500 K en faisant des mesures de thermomécanique (TMA), de thermogravimétrie (TG), d'analyse thermale différentielle (DTA), et d'examen de calorimétrie différentielle (DSC). Les coefficients d'expansion thermale dans les trois directions cristallographiques fondamentales ont montré un comportement anormal près de 453 K. Aussi, près de cette température, des effets anisotropes ont été observés et pas de perte de poids n'a été détectée. Les mesures (DSC) de la chaleur spécifique à pression constante Cp, ont montré un accroissement faible et continu durant l'accroissement de température plus un sommet à 453 K