Interpretations of the real time scattering experiment for polystyrene melts during stress relaxation

We discuss observations of the static form factor St R(q) of the single chain, in amorphous polystyrene (M w = 650 000) in the submolecular range for different durations of relaxation tR after a sudden uniaxial elongation. The data resulting from these observations are given in the preceding letter to this Journal. They are displayed here in two different representations. The first is derived from a qtR1/4 superposition law for durations tR between the Rouse time and the terminal stress relaxation time, as in reference [1]. The second representation is derived from the assumed existence of a q independent relaxation time, equal to a macroscopic quantity, the terminal relaxation time.Nous discutons des observations du facteur de forme statique S tR(q) d'une chaîne dans un échantillon de polystyrène amorphe (Mw = 650 000), mesuré dans le domaine intermédiaire, pour différentes durées de relaxation tR après une déformation uniaxiale. Les valeurs du facteur de forme tirées de cette expérience sont reproduites dans la lettre précédente à ce Journal. Elles sont représentées ici de deux manières différentes. La première découle d'une loi de superposition qtR 1/4 pour des durées comprises entre le temps de Rouse et le temps terminal de relaxation de la contrainte [1]. La seconde découle de l'existence supposée, à grand q, d'un temps de relaxation indépendant de q, c'est-à-dire de l'échelle d'observation, et égal au temps terminal