Structural defects in YBa2Cu2CoO6+x and YBaCuCoO5

YBa2Cu2CoO6+x and YBaCuCoO5 were prepared at 900 ° C. Tetragonal unit cells determined by electron and x-ray diffraction: YBa 2Cu2CoO6+x prepared in air, a = 3.88, c = 11.66 Å and YBaCuCoO5, a = 3.87, c = 7.56 Å. A variation in c of 11.61 to 11.73 Å was caused by the oxygen non-stoichiometry in YBa2Cu 2CoO6+x. The unit cell size of YBaCuCoO5 was constant, indicating a stoichiometric phase. Imaging and electron diffraction reveal that the triple-layer perovskite YBa2Cu2CoO6+x contains double-layer defects, while the double-layer structure of YBaCuCoO5 exhibits triple-layer defects. X-ray microanalysis indicated defects with a decreased Ba/Y ratio in YBa2Cu2CoO6+x and an increased Ba/Y ratio in YBaCuCoO5. The Co/Y ratios remained fairly constant in both compounds, when defect and well-ordered areas were compared.YBa2Cu2CoO6+x et YBaCuCoO5 ont été préparés à 900 °C. Des mailles unitaires tétragonales ont été déterminées par microscopie électronique et diffraction des rayons X: YBa2Cu2CoO6+x préparé à l'air, a = 3,88, c = 11, 66 Å et YBaCuCoO5, a = 3,87 et c = 7,56 Å. Une variation de 11,61 à 11,73 Å pour c est causée par la non stoéchiométrie de l'oxygène dans YBa2Cu 2CoO6+x. La taille de la maille unitaire de YBaCuCoO5 restant constante semble confirmer une phase stoichiométrique. Des images et la diffraction électroniques montrent que la triple couche perovskite YBa2Cu2CoO6+x contient des doubles couches de défauts tandis que la structure en double couche de YBaCuCoO5 montre des triples couches de défauts. La microanalyse X révèle des défauts avec un rapport Ba/Y décroissant pour YBa2Cu2CoO6+x et un rapport croissant pour YBaCuCoO5. Le rapport Co/Y reste pratiquement constant dans les 2 structures quand les zones fautées ou bien ordonnées sont comparées