Élaboration et caractérisation de cristaux dérivés de K$_{3}$Li$_{2}$Nb$_{5}$O$_{15}$

Good quality crystals of K$_{3}$Li$_{2}$Nb$_{5}$O$_{15}$ type were grown from the melt followed by method slow cooling using a pseudo-flux method (an excess of K$_{2}$CO$_{3}$ and Nb$_{2}$O$_{5}$ is present). The crystals were identified by X-ray diffraction, they crystallized with the tungsten bronze-type structure in the tetragonal system at room temperature. The space group is P4bm. Their composition (K$_{2.82}$(Nb–O)$_{0.08}$Li$_{1.54}$Nb$_{5}$O$_{15}$) was determined by chemical analysis. Dielectric measurements were realized along the [001] and [100] directions in the frequency range from 10$^{3}$ to $3 \times 10^{5}$ Hz. The temperature dependences of dielectric constants $\varepsilon^{\prime}_{\rm r33}$ and $\varepsilon^{\prime}_{\rm r11}$ and of birefringence $\Delta n$ show two maximums at $T_{1}\cong 100$ K and $T_{\rm C}\cong 680$ K, the latter being the ferroelectric Curie temperature.Des cristaux de bonne qualité de type K$_{3}$Li$_{2}$Nb$_{5}$O$_{15}$ et de structure “bronze” ont été élaborés par fusion et refroidissement lent en présence d'un pseudo-flux (K$_{2}$CO$_{3}$ et Nb$_{2}$O$_{5}$ en excès). L'analyse chimique montre que leur composition correspond à la formulation K$_{2,82}$(Nb–O)$_{0,08}$Li$_{1,54}$Nb$_{5}$O$_{15}$. Ces matériaux cristallisent dans le système quadratique à 295 K avec le groupe spatial P4bm. Les mesures diélectriques ont été effectuées selon deux directions [001] et [100], perpendiculaires aux grandes faces des cristaux élaborés. Les variations thermiques de la permittivité et de la biréfringence ont permis de mettre en évidence deux maxima l'un à $T_{1}\cong 100$ K selon [100], l'autre à $T_{\rm C}\cong 680$ K selon [001] ; ce dernier correspond à al température de Curie ferroélectrique