Influence Of Chemical Degradation And Abrasion On Surface Properties Of Nanorestorative Materials

Aim: The aim of this in vitro study was to investigate the synergistic effect of chemical degradation (erosion) and three-body abrasion (mechanical degradation) on the surface roughness (Ra) and hardness (KHN) of two nanorestorative materials and two conventional materials. Methods: Discshaped specimens (5 mm in diameter, 2 mm thick) of Filtek Z350™ and TPH Spectrum™ composites and Ketac Nano™ and Vitremer™ light-curing glass ionomer cements, nanomaterials and conventional materials were prepared according to the manufacturer's instructions. After 24 h, polishing procedures were performed and initial measurements of Ra and KHN were taken in all specimens. The specimens were divided into 12 groups (n = 10) according to material and storage media: artificial saliva, orange juice, and Coca-Cola®. After 30 days of storage, the specimens were submitted to mechanical degradation and re-evaluated for Ra and KHN. Data were tested for significant differences by repeated-measure three-way ANOVA and Tukey's tests (p