Add to ORKGThe fracture resistance of endodontically treated teeth has been an obstacle to the durability of the remaining teeth and restorations. The aim of this study was to evaluate the fracture resistance of endodontically treated bovine and human teeth that were restored with either prefabricated metal posts, glass fiber posts, or composite resin cores. Statistical analysis revealed significant difference between different substrates, but there was no statistically significant difference between different types of intraradicular posts or in the interaction between substrate and post types. The intraradicular posts do not increase the fracture resistance of endodontically treated teeth. The metal posts presented more unfavorable fracture modes whe...
(1) Background: The study aimed to compare and analyse the differences between the features of prefa...
The purpose of this study was to evaluate the fracture strength and mode of failure of endodonticall...
This study compared the fracture strength of different conditioned metallic posts, fiber-reinforced-...
The fracture resistance of endodontically treated teeth has been an obstacle to the durability of th...
AbstractBackground/purposeThe aim of this study was to determine and compare the fracture resistance...
Recent formulations of resin-based composites have incorporated different combinations of materials....
Background/purpose: The aim of this study was to determine and compare the fracture resistance of en...
Reasons for the failed endodontic teeth which had an extensive restoration can be attributed to the ...
AbstractThe restoration of endodontically treated teeth requires the fabrication of a post and core ...
Background: Posts and cores are often required for restoration of pulpless teeth and to provide ret...
Statement of problem. Dental fractures can occur in endodontically treated teeth restored with posts...
Background and Aim : Prefabricated posts are advantageous in restoring endodontically treated teeth ...
INTRODUCTION: Prefabricated metal and ceramic posts can be used with different kinds of core materia...
Abstract Objective This study evaluated the fracture resistance of endodontically treated teeth re...
This study evaluated the fracture resistance of endodontically treated teeth restored with prefabric...
(1) Background: The study aimed to compare and analyse the differences between the features of prefa...
The purpose of this study was to evaluate the fracture strength and mode of failure of endodonticall...
This study compared the fracture strength of different conditioned metallic posts, fiber-reinforced-...
The fracture resistance of endodontically treated teeth has been an obstacle to the durability of th...
AbstractBackground/purposeThe aim of this study was to determine and compare the fracture resistance...
Recent formulations of resin-based composites have incorporated different combinations of materials....
Background/purpose: The aim of this study was to determine and compare the fracture resistance of en...
Reasons for the failed endodontic teeth which had an extensive restoration can be attributed to the ...
AbstractThe restoration of endodontically treated teeth requires the fabrication of a post and core ...
Background: Posts and cores are often required for restoration of pulpless teeth and to provide ret...
Statement of problem. Dental fractures can occur in endodontically treated teeth restored with posts...
Background and Aim : Prefabricated posts are advantageous in restoring endodontically treated teeth ...
INTRODUCTION: Prefabricated metal and ceramic posts can be used with different kinds of core materia...
Abstract Objective This study evaluated the fracture resistance of endodontically treated teeth re...
This study evaluated the fracture resistance of endodontically treated teeth restored with prefabric...
(1) Background: The study aimed to compare and analyse the differences between the features of prefa...
The purpose of this study was to evaluate the fracture strength and mode of failure of endodonticall...
This study compared the fracture strength of different conditioned metallic posts, fiber-reinforced-...