The article touches upon the reasons of cracks formation in a vertical steel tank wall used in oil transportation. Here are given the comparative research results of chemical composition and mechanical properties of steel, used in manufacture of the flat product: tensile strength, yield strength, impact strength and hardness
The influence of environmental medias on crack propagation of a structural steel at high and very-hi...
AbstractThe unexpected failure of different structure components subjected to aggressive hydrogen en...
SIGLELD:0678.231F(AD-A--106-116)(microfiche). / BLDSC - British Library Document Supply CentreGBUnit...
The paper provides results of studying a change in mechanical properties of the design elements meta...
AbstractThis paper describes the fatigue properties of chromium-molybdenum steel in air and diesel o...
The present research deals with external surface cracks in vertical steel tanks. Such defects occur ...
Rotary bending fatigue tests were performed in laboratory air and 3.5% NaCl aqueous solution to inve...
Various storage tanks are used by petroleum industries for storing crude and its fractions as the fe...
In this paper, the fatigue performance of three types of epoxy coatings (pure, Novolac and reinforce...
Under strong earthquake motions, the liquid stored within large unanchored steel tanks can cause roc...
Corrosion medium such as CO2-Cl-causing corrosion pits in the pipe wall exist usually in the service...
1055657182626790Final reportPDFTech ReportDOT/FRA/ORD-06/04.IDOT-VNTSC-FRA-02-03DB034/RR28Alloy stee...
There the design data about the thermal stresses in the tank walls on the level in interface of acid...
ABSTRACT. Long term service of oil and gas trunk pipelines in corrosion and hydrogenated environment...
The article presents the preliminary tests results of three high-strength steels, which are used in ...
The influence of environmental medias on crack propagation of a structural steel at high and very-hi...
AbstractThe unexpected failure of different structure components subjected to aggressive hydrogen en...
SIGLELD:0678.231F(AD-A--106-116)(microfiche). / BLDSC - British Library Document Supply CentreGBUnit...
The paper provides results of studying a change in mechanical properties of the design elements meta...
AbstractThis paper describes the fatigue properties of chromium-molybdenum steel in air and diesel o...
The present research deals with external surface cracks in vertical steel tanks. Such defects occur ...
Rotary bending fatigue tests were performed in laboratory air and 3.5% NaCl aqueous solution to inve...
Various storage tanks are used by petroleum industries for storing crude and its fractions as the fe...
In this paper, the fatigue performance of three types of epoxy coatings (pure, Novolac and reinforce...
Under strong earthquake motions, the liquid stored within large unanchored steel tanks can cause roc...
Corrosion medium such as CO2-Cl-causing corrosion pits in the pipe wall exist usually in the service...
1055657182626790Final reportPDFTech ReportDOT/FRA/ORD-06/04.IDOT-VNTSC-FRA-02-03DB034/RR28Alloy stee...
There the design data about the thermal stresses in the tank walls on the level in interface of acid...
ABSTRACT. Long term service of oil and gas trunk pipelines in corrosion and hydrogenated environment...
The article presents the preliminary tests results of three high-strength steels, which are used in ...
The influence of environmental medias on crack propagation of a structural steel at high and very-hi...
AbstractThe unexpected failure of different structure components subjected to aggressive hydrogen en...
SIGLELD:0678.231F(AD-A--106-116)(microfiche). / BLDSC - British Library Document Supply CentreGBUnit...
DOI
Add to ORKG