The internal friction of α-LuH(D)x, with 0 ≤ x ≤ 0.2, has been measured in the range 4.2 ≤ T ≤ 450 K both in the annealed state and after deformation. Three main peaks were observed and designated according to their characteristics : (1) "H"-peak - at 215-225K, with an x-dependent amplitude and an isotope-dependent temperature ; (2) "d-H"-peak - at 250-260 K, appears after deformation in the H(D)-containing samples only ; (3) "d"-pea
A torsional internal friction measurement was performed for Nb single crystals containing N-H and O-...
Anelasticity, as suggested by Zener /1/ in 1948, gives rise to internal friction which is independen...
The heat capacity of high purity electrotransport refined lutetium was measured between 1 and 20/sup...
The internal friction and the dynamic modulus have been measured between 4.2 and 470 K in the system...
In order to clarify the nature of the numerous thermally activated processes occurring in yttrium, t...
The internal friction of pure Ti between 500K and 700K is constant at 10-4when measured during a con...
The results of influencing of hydrogen at simultaneous influence of ultrasonic deformation on intern...
The internal friction of V-1 at. % H alloys (M : Ti, Zr, Mo, Nb, Cr, Fe and Cu) has been measured ov...
Linear and non-linear internal friction and the effective Young’s modulus of a Ni50.8Ti49.2 alloy ha...
Linear and non-linear internal friction and the effective Young’s modulus of a Ni50.8Ti49.2 alloy ha...
The linear and non-linear internal friction, effective Young’s modulus, and amplitude-dependent modu...
Nous présentons un nouveau pic de relaxation anélastique dans le système V-H.A new anelastic relaxat...
The linear and non-linear internal friction, effective Young’s modulus, and amplitude-dependent modu...
Modeling hydrogen-induced embrittlement in metals requires a clear understanding of the effects of h...
Abstract. In order to clarify the nature of the numerous thermally activated processes occurring in ...
A torsional internal friction measurement was performed for Nb single crystals containing N-H and O-...
Anelasticity, as suggested by Zener /1/ in 1948, gives rise to internal friction which is independen...
The heat capacity of high purity electrotransport refined lutetium was measured between 1 and 20/sup...
The internal friction and the dynamic modulus have been measured between 4.2 and 470 K in the system...
In order to clarify the nature of the numerous thermally activated processes occurring in yttrium, t...
The internal friction of pure Ti between 500K and 700K is constant at 10-4when measured during a con...
The results of influencing of hydrogen at simultaneous influence of ultrasonic deformation on intern...
The internal friction of V-1 at. % H alloys (M : Ti, Zr, Mo, Nb, Cr, Fe and Cu) has been measured ov...
Linear and non-linear internal friction and the effective Young’s modulus of a Ni50.8Ti49.2 alloy ha...
Linear and non-linear internal friction and the effective Young’s modulus of a Ni50.8Ti49.2 alloy ha...
The linear and non-linear internal friction, effective Young’s modulus, and amplitude-dependent modu...
Nous présentons un nouveau pic de relaxation anélastique dans le système V-H.A new anelastic relaxat...
The linear and non-linear internal friction, effective Young’s modulus, and amplitude-dependent modu...
Modeling hydrogen-induced embrittlement in metals requires a clear understanding of the effects of h...
Abstract. In order to clarify the nature of the numerous thermally activated processes occurring in ...
A torsional internal friction measurement was performed for Nb single crystals containing N-H and O-...
Anelasticity, as suggested by Zener /1/ in 1948, gives rise to internal friction which is independen...
The heat capacity of high purity electrotransport refined lutetium was measured between 1 and 20/sup...