STRESS DEPENDENT INTERNAL FRICTION AND MODULUS CHANGES IN IRON BASED METALLIC GLASSES

The measurements were made in a torsional pendulum at about 0.1 cps using longitudinal stress (5 - 150 MPa) in the temperature range 20 - 600°C. The internal friction (i.f.) decreases and the modulus increases monotonously with increasing longitudinal stress in the, amorphous state. This i.f. change is more pronounced in the temperature range of structural relaxation. Changing the stress at constant temperature the changes of the measured parameters were time and temperature dependent. These effects can be explained by the diffusion controlled reversible ordering of the atoms due to the applied stress. Also the isothermal crystallization was accelerated by the stress