Synthesis, characterization andin vitro degradation of PLLA

The study and application of bioreabsorbable polyesters to repair damaged tissues is a promising research area. Poly(L-lactic acid), PLLA, is the most important bioreabsorbable polyester due to it excellent biocompatibility and bioreabsorption. The aim of this work was to synthesize, characterize and evaluate the in vitro degradation process of PLLA membranes. The polymer was synthesized by ring opening of the cyclic diester of lactic acid, using as catalyst Sn(Oct)2. PLLA presented high values of molar mass (Mw around 10(5) g/mol) and its chemical structure was confirmed by RMN ¹H, 13C and IR. The thermal properties of PLLA were studied by DSC, from which a high cristallinity degree was observed, consistent with the literature. The in vitro degradation of PLLA membranes demonstrated that the crystallinity degree increased with increasing degradation times.O estudo e aplicação de poliésteres bioreabsorvíveis para reparar tecidos danificados tem se mostrado uma área de pesquisa muito promissora. Poli (L-ácido láctico), PLLA, se destaca dentre os poliésteres bioreabsorvíveis, em função de características como biocompatibilidade e bioreabsorção. No entanto, seu alto custo de importação limita a expansão de seus dispositivos no País. Os objetivos deste trabalho foram sintetizar, caracterizar e estudar a degradação in vitro de membranas de PLLA. O polímero foi sintetizado através da abertura do dímero cíclico do ácido láctico, utilizando-se como catalisador Sn(Oct)2. Obteve-se PLLA com altos valores de massa molar (Mw em torno de 10(5) g/mol) e sua estrutura química foi confirmada através de RMN de ¹H e 13C e IR. As propriedades térmicas do PLLA foram estudadas por DSC, sendo verificada uma alta cristalinidade para o material, o que está de acordo com a literatura. O estudo da degradação in vitro das membranas do PLLA mostrou um aumento do grau de cristalinidade em função do tempo de degradação.263