Aging heat treatment effect on the microstructure and impact properties of the super-austenitic stainless steel ASTM A 744 Gr. CN3MN

This research investigated the influence of solution heat treatments on the microstructure and properties of this type of material. These treatments were carried out at temperatures ranging from 1100 to 1250ºC. Impact (Charpy) tests were conducted at room temperature and -46°C for all solution treated samples. The microstructural analyses were carried out by scanning electron microscopy, transmission electron microscopy and X-ray diffraction. It was concluded that, to maximize the material's impact strength, the solution heat treatment should be done at 1200ºC, at which temperature the volumetric fraction of precipitates is lower than at other solution heat treatment temperatures. The samples that were solution heat treated at 1200 and 1240ºC presented sigma (s) and M6C carbide phases.O aço inoxidável superaustenítico ASTM A 744 Gr. CN3MN é aplicado na fabricação de equipamentos que trabalham em ambientes sob corrosão severa com solicitação mecânica. Nesse trabalho investigou-se a influência do tratamento térmico de solubilização na microestrutura e nas propriedades desse tipo de material. Foram realizados tratamentos térmicos de solubilização na faixa de temperaturas entre 1100 e 1250°C. Ensaios de impacto (Charpy) em temperatura ambiente e a -46°C foram realizados nas amostras tratadas termicamente. As análises microestruturais foram feitas por meio de microscopia eletrônica de varredura, eletrônica de transmissão e difração de raios X. Concluiu-se que, para maximizar a resistência ao impacto, a solubilização deve ser feita a 1200°C, pois tal medida produz a menor fração volumétrica de precipitados. As amostras solubilizadas a 1200 e 1240°C apresentaram fase sigma (s) e carboneto M6C.132