Microstructure and inhomogeneous fuel trapping at divertor surfaces in the JET tokamak

The plasma deposited layers at divertor surfaces in the JET tokamak with carbon wall have been studied post mortem, using micro ion beam analysis (µ-IBA) methods, optical microscopy and scanning electron microscopy (SEM). The layers were formed during plasma operations over different periods through 1998-2009. They frequently have a columnar structure. For µ-IBA a 3 MeV 3He beam was used, focused to about 5-15 µm size. Nuclear reaction analysis was used to measure D, Be and C. Elemental mapping was carried out both at the original surface and on polished layer cross sections. Trapped deuterium is predominantly found in remote areas on the horizontal bottom divertor tiles and in regions with locally enhanced deuterium concentration on the vertical tiles. Pockets with enhanced deuterium concentration are found in the carbon fibre composite (CFC) substrate. Areas with dimensions of about 100 µm with enhanced deuterium concentration are also found inside the deposited layers. The inhomogeneous fuel trapping is tentatively explained with co-deposition in partly protected pits in the substrate and by incorporation of dust particles in the growing layer