The DC and AC conductivity studies of As-Se glasses over a wide range of compositions have been reported and discussed. The contribution to conductivity from transport among extended states has been delineated and the possible existence of a characteristic temperature is indicated. Two conductivity maxima have been observed as a function of composition in AC conductivities at lower temperatures
DC and AC resistivities of some silicate glasses containing both As3+ and As5+ ions have been measur...
A number of chalcogenide glasses, representing the complete glass forming regions of the· three bina...
Electrical conductivity data (from 200 to 360 K) on fifteen glass compositions of the As-Ag-Te syste...
The DC and AC conductivity studies of As---Se glasses over a wide range of compositions have been re...
The low and high temperature DC and AC conductivities of As-Se-Te glasses have been studied with dif...
Results of the d. c. electrical conductivity (6) measurements (from 90 to 420K) on13; fifteen glass ...
The arsenic (As) to selenium (Se) ratio in AsxSe1-x glasses ranging from x = 0.2 to 0.5 was varied i...
A.C. conductivity σac of amorphous As40+xSe60-x and As2Se3 : Ag has been measured. The σac of these ...
The I-V characteristics of bulk As40Te60-xSex and As35Te65-xSex glasses have been studied with a cur...
Se films were prepared by thermal evaporation technique in thickness range 150-8500 Angstrom. X-ray ...
A simple theory of electrical conductivity of a-As2Se3 and similar amorphous semiconductor has been ...
661-667DC electrical properties of the system Se100-X InX (where x =5, 10, 15 and 20 at. %) have ...
Measurements of the dielectric properties and the a.c. conductivity of glassy As2Se3 are reported. A...
AC conductivity and dielectric properties of sulphate glasses have been studied as a function of tem...
$Te_{42}As_{36}Ge_{10}Si_{12}$ chalcogenide composition was prepared by conventional melt-quenching....
DC and AC resistivities of some silicate glasses containing both As3+ and As5+ ions have been measur...
A number of chalcogenide glasses, representing the complete glass forming regions of the· three bina...
Electrical conductivity data (from 200 to 360 K) on fifteen glass compositions of the As-Ag-Te syste...
The DC and AC conductivity studies of As---Se glasses over a wide range of compositions have been re...
The low and high temperature DC and AC conductivities of As-Se-Te glasses have been studied with dif...
Results of the d. c. electrical conductivity (6) measurements (from 90 to 420K) on13; fifteen glass ...
The arsenic (As) to selenium (Se) ratio in AsxSe1-x glasses ranging from x = 0.2 to 0.5 was varied i...
A.C. conductivity σac of amorphous As40+xSe60-x and As2Se3 : Ag has been measured. The σac of these ...
The I-V characteristics of bulk As40Te60-xSex and As35Te65-xSex glasses have been studied with a cur...
Se films were prepared by thermal evaporation technique in thickness range 150-8500 Angstrom. X-ray ...
A simple theory of electrical conductivity of a-As2Se3 and similar amorphous semiconductor has been ...
661-667DC electrical properties of the system Se100-X InX (where x =5, 10, 15 and 20 at. %) have ...
Measurements of the dielectric properties and the a.c. conductivity of glassy As2Se3 are reported. A...
AC conductivity and dielectric properties of sulphate glasses have been studied as a function of tem...
$Te_{42}As_{36}Ge_{10}Si_{12}$ chalcogenide composition was prepared by conventional melt-quenching....
DC and AC resistivities of some silicate glasses containing both As3+ and As5+ ions have been measur...
A number of chalcogenide glasses, representing the complete glass forming regions of the· three bina...
Electrical conductivity data (from 200 to 360 K) on fifteen glass compositions of the As-Ag-Te syste...