Add to ORKGFatigue is associated with the deterioration caused by applying repeated loads, and is affected by temperature or aging. Generally, time sweep tests are used to simulate fatigue, in order to obtain the fatigue laws. However, this requires too much time, often preventing its use. A method to estimate the fatigue laws from a strain sweep test is presented. The test was performed on a semi-dense mixture with different types of binder (unconditioned or aged) tested at different temperatures. This test is able to estimate fatigue laws more quickly, allowing the effect of different factors on the mixtures' fatigue life to be studied.Peer Reviewe
Modelling of mechanical behaviour of asphalt pavements has been fundamentally based on bituminous ma...
One of the most important parameters to define bituminous mixture behavior in service is the toughne...
The objective of this paper is to reveal the effects of aging on the fatigue performance of asphalt ...
Fatigue is associated with the deterioration caused by applying repeated loads, and is affected by t...
Fatigue cracking of bituminous mixtures is closely related to the loss of ductility produced by the ...
This paper reports the experimental investigation conducted to study the influence of temperature an...
The fatigue life of a bituminous mixture is usually obtained by fatigue testing or a surrogate model...
Fatigue cracking is a major problem in bituminous pavements. The bitumen and mastic properties infl...
Bitumen ageing plays a significant role in determining the resistance of asphalt mixes to fatigue cr...
Fatigue characterization of asphalt mixtures is a very important issue. However, existing techniques...
The ageing of asphalt mixes, together with their exposure to low temperatures, causes a progressive ...
The EBADE test has been developed at the Road Research Laboratory of the UPC-Barcelona Tech to asses...
This paper presents the results of a study where the fatigue life of a dense bituminous mixture was ...
This paper compares the results obtained in two types of cyclic tension-compression tests, a time sw...
The characterization of fatigue damage on bituminous materials under cyclic loading has been classic...
Modelling of mechanical behaviour of asphalt pavements has been fundamentally based on bituminous ma...
One of the most important parameters to define bituminous mixture behavior in service is the toughne...
The objective of this paper is to reveal the effects of aging on the fatigue performance of asphalt ...
Fatigue is associated with the deterioration caused by applying repeated loads, and is affected by t...
Fatigue cracking of bituminous mixtures is closely related to the loss of ductility produced by the ...
This paper reports the experimental investigation conducted to study the influence of temperature an...
The fatigue life of a bituminous mixture is usually obtained by fatigue testing or a surrogate model...
Fatigue cracking is a major problem in bituminous pavements. The bitumen and mastic properties infl...
Bitumen ageing plays a significant role in determining the resistance of asphalt mixes to fatigue cr...
Fatigue characterization of asphalt mixtures is a very important issue. However, existing techniques...
The ageing of asphalt mixes, together with their exposure to low temperatures, causes a progressive ...
The EBADE test has been developed at the Road Research Laboratory of the UPC-Barcelona Tech to asses...
This paper presents the results of a study where the fatigue life of a dense bituminous mixture was ...
This paper compares the results obtained in two types of cyclic tension-compression tests, a time sw...
The characterization of fatigue damage on bituminous materials under cyclic loading has been classic...
Modelling of mechanical behaviour of asphalt pavements has been fundamentally based on bituminous ma...
One of the most important parameters to define bituminous mixture behavior in service is the toughne...
The objective of this paper is to reveal the effects of aging on the fatigue performance of asphalt ...