Microstructure and mechanical properties of heat-resistant 12 % Cr ferritic-martensitic steel EK-181 after thermomechanical treatment

The effect of high-temperature thermomechanical treatment (TMT) with the deformation in the austenitic region on the features of microstructure, phase transformations and mechanical properties of low-activation 12% Cr ferritic-martensitic steel EK-181 is investigated. It is established, that directly after thermomechanical treatment (without tempering) the sizes and density of V(CN) particles are comparable with those after a traditional heat treatment (air quenching and tempering at 720°C, 3 h), where these particles are formed only during tempering. It causes the increasing of the yield strength of the steel up to ≈1450 MPa at room temperature and up to ≈430 MPa at the test temperature T = 650°C. The potential of microstructure modification by this treatment aimed at improving heat resistance of steel is discussed