Влив попередньої обробки волокон льону на показники целюлози

The influence of the main process parameters (temperature, duration, irrigation modulus, catalyst content) alkaline and acid treatment of flax fibers on the quality parameters of the obtained pulp was investigated. The effect of various chemical agents on removing non-cellulose components of flax fibers, in particular minerals, was studied. It was found that during alkaline treatment of the flax fibers sodium hydroxide better removed lignin and minerals than potassium hydroxide and hydrous ammonia.For the production of microcrystalline cellulose of flax fibers, it is recommended to carry out alkaline treatment at the concentration of sodium hydroxide in 20-25 % solution at the temperature of 160 0С for 180 minutes.The preliminary stage of acid hydrolysis of flax fibers is recommended to be carried out with a sulfuric acid concentration of 1 % at 100 0С for 180 minutes.Исследован процесс щелочной и кислотной обработки на показатели качества льняных волокнистых полуфабрикатов. Определены оптимальные условия проведения щелочной и кислотной обработки волокон льна. Установлено, что обработка волокон льна в щелочной и кислой среде удаляет лигнин и минеральные вещества из волокон льна и рекомендуется для использования в производстве микрокристаллической целлюлозы. Досліджено процес лужної та кислотної обробки на показники якості лляних волокнистих напівфабрикатів. Визначено оптимальні умови проведення лужної та кислотної обробки волокон льону. Встановлено, що обробка волокон льону у лужному і кислому середовищі видаляє лігнін і мінеральні речовини з волокон льону та рекомендується для використання у виробництві мікрокристалічної целюлози