Comparison of acellular and cellular bioactivity of poly 3-hydroxybutyrate/hydroxyapatite nanocomposite and poly 3-hydroxybutyrate scaffolds

Nanocomposites have recently been identified as a useful scaffolding material in tissue engineering applications. Poly (3-hydroxybutyrate)/hydroxyapatite nanoparticles (P3HB)/(nHA) porous scaffolds were successfully fabricated through a solvent casting and particulate leaching technique. P3HB/nHA and P3HB scaffolds were prepared by the same technique for comparison. The structure of the nanocomposite and P3HB scaffolds was observed by SEM. The Energy Disperssive X-ray Analysis (EDXA, map of Ca) results indicated that HA nanoparticles were homogeneously dispersed in the P3HB matrix. X-ray diffraction (XRD) analysis showed that P3HB and HA coexist in the nanocomposite. Transmission electron microscopy (TEM) images also showed that the particle size of HA was 30 similar to 40 nm. The porosity of the scaffolds was 84%, and macropores and micropores coexisted and interconnected throughout the scaffolds. Acellular bioactivity experiments showed that more HA crystals formed on the surface of the nanocomposite scaffold than on the P3HB scaffold after 4 weeks immersion in Simulated Body Fluid (SBF). Cell culture experiments demonstrated that the P3HB/nHA nanocomposite scaffold had a better tendency of proliferation and Alkaline Phosphatase (ALP) activity to MG 63 cells than the pure P3HB scaffold. It was found that nHA addition can improve acellular and cellular bioactivity of the P3HB scaffold