6-amino-m-kresol polimerinin bakır ve paslanmaz çelik üzerine sentezi ve korozyon performansının incelenmesi

TEZ7165Tez (Yüksek Lisans) -- Çukurova Üniversitesi, Adana, 2009.Kaynakça (s.74-79) var.x, 80 s. : res. ; 29 cm.In this study, the polymerization and corrosion performance of 6-amino-mcresol, aniline and 6-amino-m-cresol coated copper electrodes were investigated on copper in chloride solution. Further, the corrosion performance of poly-6-amino-mcresol coated stainless steel electrode were investigated in acidic solution. The cyclic voltammetry technique was used to synthesis polymer film. The corrosion potentials of polymer films coated electrodes were determined and Nyquist diagrams of the polymer films coated electrodes were obtained. The three electrode technique was used to for the all experiments. Equivalent circuit models were proposed for bare and polimer films coated electrodes. Poly-AmC coated on stainless steel and Polyaniline/ poly-AmC coated on copper electrodes exhibited important barrier properties.Bu çalışmada; bakır üzerine 6-amino-m-kresol, anilin ve anilin üzerine 6- amino-m-kresol polimeri oluşturulmuş ve bunların klorürlü ortamdaki korozyon performansı incelenmiştir. Ayrıca, paslanmaz çelik elektrot üzerine 6-amino-mkresol sentezlenerek asidik ortamdaki korozyon performansı incelenmiştir. Polimer sentezleri için dönüşümlü voltametri (CV) tekniği kullanılmıştır. Polimer kaplanan elektrotların, korozyon potansiyelleri belirlenmiş ve AC yöntemiyle de Nyquist diyagramları elde edilmiştir. Tüm deneylerde üç elektrot tekniği kullanılmıştır. Polimer kaplanan ve kaplamasız elektrotlar için eşdeğer devre modeli önerilmiştir. Paslanmaz çelik yüzeyine sentezlenen poli-AmC ve bakır üzerine sentezlenen polianilin/ poli-AmC kaplama sisteminin önemli bir bariyer özelliği sergilediği anlaşılmıştır.Bu çalışma Ç.Ü. Bilimsel Araştırma Projeleri Birimi Tarafından Desteklenmiştir. Proje No:FEF2008YL