Testing the responses of membranes made of FeS: Ag2S: PTFE : bachelor thesis

U radu su pripremljene heterogene membranske elektrode i potenciometrijsko određivanje željezovih(II) kationa pri pH=4,00 te pH=4,75. Mjerenja su rađena za svaku membranu kako bi se dobile granice dokazivanja i granica određivanja Fe 2+ iona. Membrane koje su se koristile za testiranje metodom slijednog razrjeđivanja tijekom završnog rada sljedećeg su sastava: Membrana 1: FeS:Ag 2 S:PTFE=1:1:2, veličina 100-125 µm Membrana 2: FeS:Ag 2 S:PTFE=1:1:2, veličina 45-100 µm Membrana 3: FeS:Ag 2 S:PTFE=1:2:3, veličina 45-100 µm Membrana 4: FeS:Ag 2 S:PTFE=1:3:4, veličina 45-100 µm Membrana 5: FeS:Ag 2 S:PTFE=1:4:5, veličina 45-100 µm Membrana 6: FeS:Ag 2 S:PTFE=1:5:6, veličina 45-100 µm Membrane su se ispitivale na odziv na ione u elektrokemijskoj ćeliji koristeći otopinu željezovog(II) sulfata heptahidrata za određivanje željezovih iona metodom slijednog razrjeđivanja. Za ispitivanje odziva i određivanje osjetljivosti na željezove ione, provedena je potenciometrijska metoda kao metoda koja se često koristi radi pristupačnosti, jednostavnosti i niske cijene.In this thesis the main goal was to prepare heterogenic membrane electrodes and potentiometric defining in pH=4,00 and pH=4,75. The measurements were done for each membrane to obtain the limits of detection and determination limit of Fe 2+ ions. The membranes that were used were made of: Membrane 1: FeS:Ag 2 S:PTFE=1:1:2, size 100-125 m Membrane 2: FeS:Ag 2 S:PTFE=1:1:2, size 45-100 m Membrane 3: FeS:Ag 2 S:PTFE=1:2:3, size 45-100 m Membrane 4: FeS:Ag 2 S:PTFE=1:3:4, size 45-100 m Membrane 5: FeS:Ag 2 S:PTFE=1:4:5, size 45-100 m Membrane 6: FeS:Ag 2 S:PTFE=1:5:6, size 45-100 m Membrane electrodes were tested for response on primary ion in electrochemical cell by using solution made of ferrous sulphate heptahydrate to determine Fe 2+ ions using sequential dilution method. The potentiometric method was used to test the response and specific sensitivity of Fe 2+ ions because of its practicality, simplicity and low cost