Síntesis y Estudio de Silicatos Mesoporosos Modificados con Boro

Mesoporous materials of the B-MCM-41 type were prepared. The influence of several hydrothermal treatment periods, the hydroxide source, the B content, the degree of B incorporation in the structure and the acidity material were investigated.It was confirmed that the acidity of the samples is due to the silanol nest structural defects present in the synthesized material. These species are mainly due to the introduction of B within the structure and the acidic properties may be caused by the presence of the heteroatom. In this way it was possible to obtain mesoporous materials with a moderate acidity, which is a very important feature for certain catalytic processes.Se prepararon materiales mesoporosos del tipo B-MCM-41. Se investigó la influencia de la variación del tiempo de tratamiento hidrotérmico, la fuente de hidróxido, el contenido de B, el grado de incorporación del B en la estructura y el carácter ácido del material obtenido.Se confirmó que la acidez de las muestras se debe a los silanoles nido presentes en los defectos estructurales del material sintetizado. Estas especies se generan principalmente por la introducción de B dentro de la estructura y sus propiedades ácidas pueden ser causadas por la presencia del heteroátomo. De esta manera se logró obtener una acidez moderada en los materiales mesoporosos obtenidos, característica muy importante para determinados procesos catalíticos