Superconducting properties of polycrystalline Nb nanowires templated by carbon nanotubes

Journal ArticleContinuous Nb wires, 7-15 nm in diameter, have been fabricated by sputter-coating single fluorinated carbon nanotubes. Transmission electron microscopy revealed that the wires are polycrystalline, having grain sizes of about 5 nm. The critical current of wires thicker than ~12 nm is very high (107 A/cm2) and comparable to the expected depairing current. The resistance versus temperature curves measured down to 0.3 K are well described by the Langer-Ambegaokar-McCumber-Halperin theory of thermally activated phase slips. Quantum phase slips are suppressed