Comparative study of the presence of latex and polychloroprene in the behavior of sintered powder EPDMCR, ethylene-propylenediene-monomer crumb rubber

In this work, the mechanical behavior of sintered waste material of ethylene-propylene-diene-monomer crumb rubber (EPDMCR) is analyzed, optimizing the temperature and compression pressure. The results obtained showed that an increase in temperature and compression pressure gives a significant improvement in the mechanical properties of the material. We later mixed the EPDMCR particles with different percentages of adhesives with the aim of further improving the mechanical performance obtained from the sintered particles. The adhesives used in this study were latex and polychloroprene, and the optimum mechanical performance obtained came from mixes with polychloroprene, using a mix with 50% adhesive. The study was concluded with an analysis of images of the material using a scanning electron microscope (SEM), in order to observe the EPDMCR-adhesive interaction.Crespo Amorós, JE.; Parres, F.; Nadal Gisbert, AV. (2012). Comparative study of the presence of latex and polychloroprene in the behavior of sintered powder EPDMCR, ethylene-propylenediene-monomer crumb rubber. Journal of Elastomers and Plastics. 44(2):127-144. doi:10.1177/0095244311418318127144442Osman, H., Ismail, H., & Mariatti, M. (2007). The Effect of Recycled Newspaper Content and Size on the Properties of Polypropylene (PP)/Natural Rubber (NR) Composites. Polymer-Plastics Technology and Engineering, 47(1), 23-29. doi:10.1080/03602550701575961Crespo, J. E., Parres, F., & Nadal, A. (2009). Mechanical behavior analysis of sintered products of natural rubber crumb rubber (NRCR) using adhesives. Materialwissenschaft und Werkstofftechnik, 40(3), 211-217. doi:10.1002/mawe.200900429Setua, D. K., & Gupta, Y. N. (2007). On the use of micro thermal analysis to characterize compatibility of nitrile rubber blends. Thermochimica Acta, 462(1-2), 32-37. doi:10.1016/j.tca.2007.06.004Nakason, C., Kaesaman, A., Samoh, Z., Homsin, S., & Kiatkamjornwong, S. (2002). Rheological properties of maleated natural rubber and natural rubber blends. Polymer Testing, 21(4), 449-455. doi:10.1016/s0142-9418(01)00109-xJincheng, W., Yuehui, C., & Jihu, W. (2005). Novel Reinforcing Filler: Application to Natural Rubber (NR) System. Journal of Elastomers & Plastics, 37(2), 169-180. doi:10.1177/0095244305052010Sutanto, P., Picchioni, F., Janssen, L. P. B. M., Dijkhuis, K. A. J., Dierkes, W. K., & Noordermeer, J. W. M. (2006). State of the Art: Recycling of EPDM Rubber Vulcanizates. International Polymer Processing, 21(2), 211-217. doi:10.3139/217.1906Jacob, C., Bhowmick, A. K., De, P. P., & De, S. K. (2003). Utilization of Powdered EPDM Scrap in EPDM Compound. Rubber Chemistry and Technology, 76(1), 36-59. doi:10.5254/1.3547740Jacob, C., Bhattacharya, A. K., Bhowmick, A. K., De, P. P., & De, S. K. (2003). Recycling of ethylene propylene diene monomer (EPDM) waste. III. Processability of EPDM rubber compound containing ground EPDM vulcanizates. Journal of Applied Polymer Science, 87(14), 2204-2215. doi:10.1002/app.11474Jacob, C., Bhowmick, A. K., De, P. P., & De, S. K. (2002). Studies on ground EPDM vulcanisate as filler in window seal formulation. Plastics, Rubber and Composites, 31(5), 212-219. doi:10.1179/146580102225003029Jacob, C., De, P. P., Bhowmick, A. K., & De, S. K. (2001). Recycling of EPDM waste. II. Replacement of virgin rubber by ground EPDM vulcanizate in EPDM/PP thermoplastic elastomeric composition. Journal of Applied Polymer Science, 82(13), 3304-3312. doi:10.1002/app.2189Jacob, C., De, P. P., Bhowmick, A. K., & De, S. K. (2001). Recycling of EPDM waste. I. Effect of ground EPDM vulcanizate on properties of EPDM rubber. Journal of Applied Polymer Science, 82(13), 3293-3303. doi:10.1002/app.2188Grigoryeva, O. P., Fainleib, A. M., Tolstov, A. L., Starostenko, O. M., Lievana, E., & Karger-Kocsis, J. (2004). Thermoplastic elastomers based on recycled high-density polyethylene, ethylene-propylene-diene monomer rubber, and ground tire rubber. Journal of Applied Polymer Science, 95(3), 659-671. doi:10.1002/app.21177Mathew, G. (2003). Journal of Materials Science, 38(11), 2469-2481. doi:10.1023/a:1023965420749Morin, J. E., Williams, D. E., & Farris, R. J. (2002). A Novel Method to Recycle Scrap Tires: High-Pressure High-Temperature Sintering. Rubber Chemistry and Technology, 75(5), 955-968. doi:10.5254/1.3547695Rajeev, R. S., & De, S. K. (2004). Thermoplastic Elastomers Based on Waste Rubber and Plastics. Rubber Chemistry and Technology, 77(3), 569-578. doi:10.5254/1.3547837Yehia, A. A., Mull, M. A., Ismail, M. N., Hefny, Y. A., & Abdel-Bary, E. M. (2004). Effect of chemically modified waste rubber powder as a filler in natural rubber vulcanizates. Journal of Applied Polymer Science, 93(1), 30-36. doi:10.1002/app.20349Zhang, K., Shen, H., Zhang, X., Lan, R., & Chen, H. (2009). Preparation and Properties of a Waterborne Contact Adhesive Based on Polychloroprene Latex and Styrene-Acrylate Emulsion Blend. Journal of Adhesion Science and Technology, 23(1), 163-175. doi:10.1163/156856108x344658Park, S. W., Kim, B. C., & Lee, D. G. (2009). Tensile Strength of Joints Bonded With a Nano-particle-Reinforced Adhesive. Journal of Adhesion Science and Technology, 23(1), 95-113. doi:10.1163/156856108x344063Buchman, A., Dodiuk-Kenig, H., Dotan, A., Tenne, R., & Kenig, S. (2009). Toughening of Epoxy Adhesives by Nanoparticles. Journal of Adhesion Science and Technology, 23(5), 753-768. doi:10.1163/156856108x379209Likozar, B., & Krajnc, M. (2008). A study of heat transfer during molding of elastomers. Chemical Engineering Science, 63(12), 3181-3192. doi:10.1016/j.ces.2008.03.031Yan, L., Kou, K., Ji, T., Liang, G., & Ha, E. (2007). Application of a new modified epoxy adhesive for bonding fluorine rubber to metal. Journal of Adhesion Science and Technology, 21(15), 1483-1496. doi:10.1163/156856107782844792Smitthipong, W., Nardin, M., Schultz, J., & Suchiva, K. (2007). Adhesion and self-adhesion of rubbers, crosslinked by electron beam irradiation. International Journal of Adhesion and Adhesives, 27(5), 352-357. doi:10.1016/j.ijadhadh.2006.09.010Colom, X., Carrillo, F., & Cañavate, J. (2007). Composites reinforced with reused tyres: Surface oxidant treatment to improve the interfacial compatibility. Composites Part A: Applied Science and Manufacturing, 38(1), 44-50. doi:10.1016/j.compositesa.2006.01.022Liu, L., Luo, Y., Jia, D., Fu, W., & Guo, B. (2006). Structure and Properties of Natural Rubber-Organoclay Nanocomposites Prepared by Grafting and Intercalating Method in Latex. Journal of Elastomers & Plastics, 38(2), 147-161. doi:10.1177/0095244306057425Budrugeac, P. (2001). Thermal degradation of glass reinforced epoxy resin and polychloroprene rubber: the correlation of kinetic parameters of isothermal accelerated aging with those obtained from non-isothermal data. Polymer Degradation and Stability, 74(1), 125-132. doi:10.1016/s0141-3910(01)00112-4Arayasantiparb, D., McKnight, S., & Libera, M. (2001). Compositional variation within the epoxy/adherend interphase. Journal of Adhesion Science and Technology, 15(12), 1463-1484. doi:10.1163/156856101753213312Kim, J. I., Ryu, S. H., & Chang, Y. W. (2000). Mechanical and dynamic mechanical properties of waste rubber powder/HDPE composite. Journal of Applied Polymer Science, 77(12), 2595-2602. doi:10.1002/1097-4628(20000919)77:123.0.co;2-cCepeda-Jiménez, C. M., Pastor-blas, M. M., Ferrándiz-Gómez, T. P., & Martín-Martínez, J. M. (2000). Surface Characterization of Vulcanized Rubber Treated with Sulfuric Acid and its Adhesion to Polyurethane Adhesive. The Journal of Adhesion, 73(2-3), 135-160. doi:10.1080/00218460008029303Sutanto, P., Picchioni, F., Janssen, L. P. B. M., Dijkhuis, K. A. J., Dierkes, W. K., & Noordermeer, J. W. M. (2006). EPDM rubber reclaim from devulcanized EPDM. Journal of Applied Polymer Science, 102(6), 5948-5957. doi:10.1002/app.25153Yun, J., Yashin, V. V., & Isayev, A. I. (2003). Ultrasonic devulcanization of carbon black-filled ethylene propylene diene monomer rubber. Journal of Applied Polymer Science, 91(3), 1646-1656. doi:10.1002/app.13320Yun, J., & Isayev, A. I. (2003). Recycling of roofing membrane rubber by ultrasonic devulcanization. Polymer Engineering & Science, 43(4), 809-821. doi:10.1002/pen.10067Pandey, K. ., Setua, D. ., & Mathur, G. . (2003). Material behaviour. Polymer Testing, 22(3), 353-359. doi:10.1016/s0142-9418(02)00112-5Setua, D. K. (1985). Scanning electron microscopy studies on thermo-oxidative ageing of polychloroprene rubber. Polymer Degradation and Stability, 12(2), 169-180. doi:10.1016/0141-3910(85)90075-8Ashalatha, P. V., George, K. E., & Francis, D. J. (1997). Scanning Electron Microscopic Studies of PP/EPDM/NR Ternary Blends. Journal of Elastomers & Plastics, 29(1), 92-101. doi:10.1177/009524439702900106Agarwal, K., Setua, D. K., & Sekhar, K. (2005). Scanning electron microscopy study on the influence of temperature on tear strength and failure mechanism of natural rubber vulcanizates. Polymer Testing, 24(6), 781-789. doi:10.1016/j.polymertesting.2005.03.004Nadal, A., Ferrer, C., Monzo, M., & Lopez, J. (2008). Etude des mécanismes de recyclage des caoutchoucs provenant des déchets de pneus. Annales de chimie Science des Matériaux, 33(3), 179-188. doi:10.3166/acsm.33.179-188Tripathy, A. R., Morin, J. E., Williams, D. E., Eyles, S. J., & Farris, R. J. (2002). A Novel Approach to Improving the Mechanical Properties in Recycled Vulcanized Natural Rubber and Its Mechanism. Macromolecules, 35(12), 4616-4627. doi:10.1021/ma012110bGriffith, A. A. (1921). The Phenomena of Rupture and Flow in Solids. Philosophical Transactions of the Royal Society A: Mathematical, Physical and Engineering Sciences, 221(582-593), 163-198. doi:10.1098/rsta.1921.000