Add to ORKGThe article deals with the analysis of a damaged part, which was designed for use in a mechanical clutch of a car. The crack in the part was found during the production inspection. The aim of metallographic and fractography analyses of the fracture surfaces was to discover the reasons for the crack. The reason for creating the crack was the formation of smaller cracks in the production during pressing process of the semiproduct. These cracks even grew after the following thermochemical treatment. The fracture was initiated during the straightening process of quenched part
Sleeve plate of clutch disk is studied in this paper,according to the fracture problems of sleeve pl...
A Light Utility Helicopter (LUH), in the course of a training flight, leaving the ground during the ...
This paper investigates the root cause of the formation of surface cracks on hot-rolled C-Mn constru...
The paper analyses some fractures of vehicle componentswhich have caused traffic accidents. The meth...
This article presents the failure analysis of a clutch disc in a two-ton truck. The failure part was...
This article aims to explain the reasons leading to the damage of a drill during its final grinding....
Through comprehensive analysis, crack propagated along the nitride in the form of planar clusters, w...
AbstractThis paper investigates the failure of a rocker arm shaft of a passenger car. The shaft fail...
The article presents an analysis in the field of gear wheel testing method application. The results ...
The fracture of a camshaft made of chilled cast iron, installed in a home-made Fukang car, happened ...
It was accomplished research of the structure steel which carbonitriding and subsequent heat treatme...
The root cause for cracking of rear brake components occurred during cold forming process was invest...
A few components belonging to an engine retrieved from the wreckage of crashed aircraft were sent to...
The cause of crankshaft fracture crack of a certain vehicle has been analyzed through macroscopic in...
A few components belonging to an engine retrieved from the wreckage of crashed aircraft were sent to...
Sleeve plate of clutch disk is studied in this paper,according to the fracture problems of sleeve pl...
A Light Utility Helicopter (LUH), in the course of a training flight, leaving the ground during the ...
This paper investigates the root cause of the formation of surface cracks on hot-rolled C-Mn constru...
The paper analyses some fractures of vehicle componentswhich have caused traffic accidents. The meth...
This article presents the failure analysis of a clutch disc in a two-ton truck. The failure part was...
This article aims to explain the reasons leading to the damage of a drill during its final grinding....
Through comprehensive analysis, crack propagated along the nitride in the form of planar clusters, w...
AbstractThis paper investigates the failure of a rocker arm shaft of a passenger car. The shaft fail...
The article presents an analysis in the field of gear wheel testing method application. The results ...
The fracture of a camshaft made of chilled cast iron, installed in a home-made Fukang car, happened ...
It was accomplished research of the structure steel which carbonitriding and subsequent heat treatme...
The root cause for cracking of rear brake components occurred during cold forming process was invest...
A few components belonging to an engine retrieved from the wreckage of crashed aircraft were sent to...
The cause of crankshaft fracture crack of a certain vehicle has been analyzed through macroscopic in...
A few components belonging to an engine retrieved from the wreckage of crashed aircraft were sent to...
Sleeve plate of clutch disk is studied in this paper,according to the fracture problems of sleeve pl...
A Light Utility Helicopter (LUH), in the course of a training flight, leaving the ground during the ...
This paper investigates the root cause of the formation of surface cracks on hot-rolled C-Mn constru...