Mechanical proporties of a composite produced from electroless ni plated cr and ti powders

Intermetallic materials such as NiTi, Ni3Cr2, CrTi are among advanced technology materials that have outstanding mechanical and physical properties for high temperature applications. Especially creep resistance, low density and high hardness properties stand out in such intermetallics. The microstructure, mechanical properties of %64Ni plated %32Cr and %4Ti powders were investigated using specimens produced by tube furnace sintering at 1000-1400°C temperature. A composite consisting of ternary additions, a metallic phase, NiTi and Ni3Ti have been prepared under Ar shroud and then tube furnace sintered. XRD, SEM (Scanning Electron Microscope), were investigated to characterize the properties of the specimens. Experimental results carried out for composition %64Ni plated %32Cr- %4Ti at 1300°C suggest that the best properties as 208HV and 6,87/cm3 density were obtained at 1400°