As-cast structure refinement of Ti-46Al alloy by hafnium and boron additions

The infl uence of Hf and B on the solidifi cation structure of cast Ti-46Al alloys was investigated. The results show that the coupling effect of Hf and B changes the solidifi cation structure morphology and strongly refi nes the grain size. When the Hf+B contents were increased from 0 + 0.0 to 3 + 0.2, 5 + 0.6 and 7 + 1.0 (in at. %), the solidification structure morphology changed from coarse columnar dendrite to fine columnar dendrite, then to equiaxed dendrite, and further to fi ne near granular grain whilst the average grain size decreased to 20 μm. It is concluded that the columnar dendrite refinement is due to the effect of Hf and B on the decrease of Al diffusion coeffi cient in the melt. The fi ne near granular grain formation is attributed to the combined constitutional supercooling formed by Al and B segregation that is strengthened by Hf and B additions at the solid/liquid interface during solidifi cation, and the TiB2 precipitates acting as heterogeneous nucle